日本大同碳素工具鋼的牌號：
油淬碳素工具鋼：YK30、YK40、YK50．
水淬碳素工具鋼：YK1、YK2、YK3、YK4、YK5、YK6、YK7．
以下是各牌號的化學成分、熱處理參數(shù)及用途例：
日本大同碳素工具鋼的牌號及化學成分匯總表
大同牌號 標準對照 化學成分
 JIS AISI VDEh C Si Mn P S Cr Mo V Ni W Co Cu 其它
油淬碳素工具鋼
YK30 SKS93   1.00~1.10 ≤0.50 0.80~1.10 ≤0.030 ≤0.030 0.20~0.60 - - ≤0.25 -  ≤0.25 -
YK40 SKS94   0.90~1.00 ≤0.50 0.80~1.10 ≤0.030 ≤0.030 0.20~0.60 - - ≤0.25 -  ≤0.25 -
YK50 SKS95   0.80~0.90 ≤0.50 0.80~1.10 ≤0.030 ≤0.030 0.20~0.60 - - ≤0.25 -  ≤0.25 -
水淬碳素工具鋼
YK1 SK140 W1  1.30~1.50 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK2 SK120 W1  1.10~1.30 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK3 SK105 W1 C105W1 1.00~1.10 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK4 SK95 W1  0.90~1.00 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK5 SK85 W1 C80W1 0.80~0.90 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK6 SK75 W1 C80W1 0.70~0.80 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
YK7 SK65 W1  0.60~0.70 ≤0.35 ≤0.50 ≤0.030 ≤0.030 ≤0.30 - - ≤0.25 - - ≤0.25 -
日本大同碳素工具鋼的牌號及熱處理參數(shù)匯總表
大同牌號 鍛造溫度℃ 熱處理溫度℃ 硬度 用途例
  退火 淬火 回火 退火HB 淬火回火HRC 
油淬碳素工具鋼
YK30 1050~850  750~780，爐冷或緩冷 790~850，油淬 150~200，空冷 ≤217 ≥63 沖裁模具，沖頭
YK40 1100~850 740~760，爐冷或緩冷 790~850，油淬 150~200，空冷 ≤212 ≥61 儀表，裁紙刀
YK50 1100~850 730~760，爐冷或緩冷 790~850，油淬 150~200，空冷 ≤212 ≥59 夾具，工具
水淬碳素工具鋼
YK1 1050~850 750~780，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤217 ≥63 刀片
YK2 1050~850 750~780，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤212 ≥63 剃須刀
YK3 1050~850 750~780，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤212 ≥63 鋼鋸，沖裁模具
YK4 1100~850 740~760，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤207 ≥61 筆尖，斧頭，鑿子
YK5 1100~850 730~760，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤207 ≥59 鋼印，圓鋸
YK6 1100~850 730~760，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤192 ≥57 鋼印
YK7 1100~850 730~760，爐冷或緩冷 760~820，水淬 150~200，空冷 ≤183 ≥56 小刀